Porous carbon spheres: Recent developments and applications

Nagesh K. Tripathi; Nagesh K. Tripathi

doi:10.3934/matersci.2018.5.1016

AIMS Materials Science

2018, Volume 5, Issue 5: 1016-1052. doi: 10.3934/matersci.2018.5.1016

Previous Article Next Article

Review Topical Sections

Porous carbon spheres: Recent developments and applications

Nagesh K. Tripathi ^,

Bioprocess Technology Division, Defence Research and Development Establishment, Jhansi Road, Gwalior-474002, India

Received: 02 August 2018 Accepted: 19 October 2018 Published: 31 October 2018

Activated or porous carbon is a carbonaceous material which has excellent adsorption capacity. Activated carbon has many applications including heavy metal and toxic gas removal as well as air and water filter applications. Microporous activated carbon in spherical shape (activated or porous carbon spheres) is a variant of activated carbon which has high compressive strength and low ash content. Pitch, polymeric (phenolic and sulfonated polystyrene resins) and other precursor materials (carbohydrate and seeds) have been generally used for production of activated carbon spheres employing carbonization and activation processes. Various parameters viz. carbonization temperature, heating rate, activation time and temperature, and activation media affected the performance and quality of end product. Generally activation by physical and chemical means is used for activated carbon spheres preparation. The use of polymeric precursors yielded better compressive strength and minimal ash content in comparison to other precursors. Activated carbon spheres produced using these processes has been successfully utilized as adsorbent materials for removal of heavy metals, organic dye, carbon dioxide, volatile organic chemicals, support for catalyst, gas and energy storage and also in chemical protective clothings. In present review, we discuss latest developments in activated carbon spheres and its use as adsorbent materials for removal of toxicants and various other applications.
- activated carbon spheres,
- carbonization; activation,
- adsorption,
- heavy metal removal,
- energy storage,
- gas storage,
- volatile organic compound removal,
- catalyst
Citation: Nagesh K. Tripathi. Porous carbon spheres: Recent developments and applications[J]. AIMS Materials Science, 2018, 5(5): 1016-1052. doi: 10.3934/matersci.2018.5.1016

Related Papers:

Abstract

Activated or porous carbon is a carbonaceous material which has excellent adsorption capacity. Activated carbon has many applications including heavy metal and toxic gas removal as well as air and water filter applications. Microporous activated carbon in spherical shape (activated or porous carbon spheres) is a variant of activated carbon which has high compressive strength and low ash content. Pitch, polymeric (phenolic and sulfonated polystyrene resins) and other precursor materials (carbohydrate and seeds) have been generally used for production of activated carbon spheres employing carbonization and activation processes. Various parameters viz. carbonization temperature, heating rate, activation time and temperature, and activation media affected the performance and quality of end product. Generally activation by physical and chemical means is used for activated carbon spheres preparation. The use of polymeric precursors yielded better compressive strength and minimal ash content in comparison to other precursors. Activated carbon spheres produced using these processes has been successfully utilized as adsorbent materials for removal of heavy metals, organic dye, carbon dioxide, volatile organic chemicals, support for catalyst, gas and energy storage and also in chemical protective clothings. In present review, we discuss latest developments in activated carbon spheres and its use as adsorbent materials for removal of toxicants and various other applications.

References

[1]	Manocha SM (2003) Porous carbons. Sadhana 28: 335–348. doi: 10.1007/BF02717142
[2]	Singh A, Lal D (2010) Preparation and characterization of activated carbon spheres from polystyrene sulphonate beads by steam and carbon dioxide activation. J Appl Polym Sci 115: 2409–2415. doi: 10.1002/app.31340
[3]	Cukierman AL (2013) Development and environmental applications of activated carbon cloths. ISRN Chem Eng 2013: 1–31.
[4]	Tripathi NK, Singh VV, Sathe M, et al. (2018) Activated carbon fabric: An adsorbent material for chemical protective clothing. Defence Sci J 68: 83–90.
[5]	Khan MK, Maclachlan MJ (2015) Polymer and carbon spheres with an embedded shell of plasmonic gold nanoparticles. ACS Macro Lett 4: 1351–1355. doi: 10.1021/acsmacrolett.5b00742
[6]	Baghel A, Singh B, Prasad GK, et al. (2011) Preparation and characterization of active carbon spheres prepared by chemical activation. Carbon 49: 4739–4744. doi: 10.1016/j.carbon.2011.06.080
[7]	Romero-Anaya AJ, Ouzzine M, Lillo-Ródenas MA, et al. (2014) Spherical carbons: Synthesis, characterization and activation processes. Carbon 68: 296–307. doi: 10.1016/j.carbon.2013.11.006
[8]	Tripathi NK, Sathe M (2017) Pilot scale production of activated carbon spheres using fluidized bed reactor and its evaluation for the removal of hexavalent chromium from aqueous solutions. J Inst Eng India Ser E 98: 141–147.
[9]	Amorós-Pérez A, Cano-Casanova L, Ouzzine M, et al. (2018) Spherical activated carbons with high mechanical strength directly prepared from selected spherical seeds. Materials 11: 770. doi: 10.3390/ma11050770
[10]	Singh A, Lal D (2008) Microporous activated carbon spheres prepared from resole-type crosslinked phenolic beads by physical activation. J Appl Polym Sci 110: 3283–3291. doi: 10.1002/app.28846
[11]	Wickramaratne NP, Jaroniec M (2013) Activated carbon spheres for CO₂ adsorption. ACS Appl Mater Inter 5: 1849–1855. doi: 10.1021/am400112m
[12]	Klefer H, Munoz M, Modrow A, et al. (2016) Polymer-based spherical activated carbon as easy-to-handle catalyst support for hydrogenation reactions. Chem Eng Technol 39: 276–284. doi: 10.1002/ceat.201500445
[13]	Boopathi M, Singh B, Vijayaraghavan R (2008) A review on NBC body protective clothing. Open Text J 1: 1–8. doi: 10.2174/1876520300801010001
[14]	Yenisoy-Karakaş S, Aygün A, Güneş M, et al. (2004) Physical and chemical characteristics of polymer-based spherical activated carbon and its ability to adsorb organics. Carbon 42: 477–484. doi: 10.1016/j.carbon.2003.11.019
[15]	Lee T, Ooi CH, Othman R, et al. (2014) Activated carbon fiber-the hybrid of carbon fiber and activated carbon. Rev Adv Mater Sci 36: 118–136.
[16]	Liu Z, Ling L, Qiao W, et al. (1999) Preparation of pitch-based spherical activated carbon with developed mesopore by the aid of ferrocene. Carbon 37: 663–667. doi: 10.1016/S0008-6223(98)00242-5
[17]	Mao H, Chen X, Huang R, et al. (2018) Fast preparation of carbon spheres from enzymatic hydrolysis lignin: Effects of hydrothermal carbonization conditions. Sci Rep 8: 9501. doi: 10.1038/s41598-018-27777-4
[18]	Nakagawa K, Mukai SR, Tamura K, et al. (2007) Mesoporous activated carbons from phenolic resins. Chem Eng Res Des 85: 1331–1337. doi: 10.1205/cherd06119
[19]	Singh A, Lal D (2006) Effect of reaction parameters on the particle sizes of crosslinked spherical phenolic beads by suspension polymerization of phenol and formaldehyde. J Appl Polym Sci 100: 2323–2330. doi: 10.1002/app.22995
[20]	Singh A, Yadav RK, Srivastava A (2009) Synthesis of resole-type phenolic beads from phenol and formaldehyde by suspension polymerization technique. J Appl Polym Sci 112: 1005–1011. doi: 10.1002/app.29480
[21]	Li R, Wang L, Shahbazi A (2015) A review of hydrothermal carbonization of carbohydrates for carbon spheres preparation. Trends Renew Energ 1: 43–56. doi: 10.17737/tre.2015.1.1.009
[22]	Liu J, Wickramaratne NP, Qiao SZ, et al. (2015) Molecular-based design and emerging applications of nanoporous carbon spheres. Nat Mater 14: 763–774. doi: 10.1038/nmat4317
[23]	Li S, Pasc A, Fierro V, et al. (2016) Hollow carbon spheres, synthesis and applications-a review. J Mater Chem A 4: 12686–12713. doi: 10.1039/C6TA03802F
[24]	Roberts AD, Li X, Zhang H (2014) Porous carbon spheres and monoliths: Morphology control, pore size tuning and their applications as Li-ion battery anode materials. Chem Soc Rev 43: 4341–4356. doi: 10.1039/C4CS00071D
[25]	Zhang P, Qiao ZA, Dai S (2015) Recent advances in carbon nanospheres: Synthetic routes and applications. Chem Commun 51: 9246–9256. doi: 10.1039/C5CC01759A
[26]	González-García P (2018) Activated carbon from lignocellulosics precursors: A review of the synthesis methods, characterization techniques and applications. Renew Sust Energ Rev 82: 1393–1414. doi: 10.1016/j.rser.2017.04.117
[27]	Moreno-Castilla C (2016) Colloidal and micro-carbon spheres derived from low-temperature polymerization reactions. Adv Colloid Interfac 236: 113–141. doi: 10.1016/j.cis.2016.08.003
[28]	Hong M, Chen J, Zhang M, et al. (2016) High-frequency fabrication of discrete and dispersible hollow carbon spheres with hierarchical porous shells by using secondary-crosslinking pyrolysis. RSC Adv 6: 16141–16149. doi: 10.1039/C5RA25932K
[29]	Wu Q, Li W, Tan J, et al. (2015) Hydrothermal synthesis of magnetic mesoporous carbon microspheres from carboxymethylcellulose and nickel acetate. Appl Surf Sci 332: 354–361. doi: 10.1016/j.apsusc.2015.01.195
[30]	Ma X, Gan L, Liu M, et al. (2014) Mesoporous size controllable carbon microspheres and their electrochemical performances for supercapacitor electrodes. J Mater Chem A 2: 8407–8415. doi: 10.1039/C4TA00333K
[31]	Ge H, Xu H, Lu T, et al. (2016) Microfluidic production of porous carbon spheres with tunable size and pores. J Colloid Interf Sci 461: 168–172. doi: 10.1016/j.jcis.2015.09.018
[32]	Huang X, Zhou LJ, Voiry D, et al. (2016) Monodisperse mesoporous carbon nanoparticles from polymer/silica self-aggregates and their electrocatalytic activities. ACS Appl Mater Inter 8: 18891–18903. doi: 10.1021/acsami.6b05739
[33]	Mhamane D, Kim MS, Park BH, et al. (2018) Orderly meso-perforated spherical and apple-shaped 3D carbon microstructures for high-energy supercapacitors and high-capacity Li-ion battery anodes. J Mater Chem A 6: 6422–6434. doi: 10.1039/C7TA11360A
[34]	Pol VG, Shrestha LK, Ariga K (2014) Tunable, functional carbon spheres derived from rapid synthesis of resorcinol-formaldehyde resins. ACS Appl Mater Inter 6: 10649–10655. doi: 10.1021/am502324m
[35]	Zhu D, Wang Y, Gan L, et al. (2015) Nitrogen-containing carbon microspheres for supercapacitor electrodes. Electrochim Acta 158: 166–174. doi: 10.1016/j.electacta.2015.01.155
[36]	Lu W, Liu M, Miao L, et al. (2016) Nitrogen-containing ultramicroporous carbon nanospheres for high performance supercapacitor electrodes. Electrochim Acta 205: 132–141. doi: 10.1016/j.electacta.2016.04.114
[37]	Anceschi A, Magnacca G, Trotta F, et al. (2017) Preparation and characterization of microporous carbon spheres from high amylose pea maltodextrin. RSC Adv 7: 36117–36123. doi: 10.1039/C7RA05343F
[38]	Tian H, Liu J, O'Donnell K, et al. (2016) Revisiting the Stӧber method: Design of nitrogen-doped porous carbon spheres from molecular precursors of different chemical structures. J Colloid Interf Sci 476: 55–61. doi: 10.1016/j.jcis.2016.05.008
[39]	Böhringer B, Guerra Gonzalez O, Eckle I, et al. (2011) Polymer-based spherical activated carbons-From adsorptive properties to filter performance. Chem Ing Tech 83: 53–60. doi: 10.1002/cite.201000166
[40]	Sun N, Sun C, Liu H, et al. (2013) Synthesis, characterization and evaluation of activated spherical carbon materials for CO₂ capture. Fuel 113: 854–862. doi: 10.1016/j.fuel.2013.03.047
[41]	Zhang C, Hatzell KB, Boota M, et al. (2014) Highly porous carbon spheres for electrochemical capacitors and capacitive flowable suspension electrodes. Carbon 77: 155–164. doi: 10.1016/j.carbon.2014.05.017
[42]	Yu Q, Guan D, Zhuang Z, et al. (2017) Mass production of monodisperse carbon microspheres with size-dependent supercapacitor performance via aqueous self-catalyzed polymerization. ChemPlusChem 82: 872–878. doi: 10.1002/cplu.201700182
[43]	Huang YP, Hsi HC, Liu SC (2013) Preparation of spherical activated phenol-formaldehyde beads from bamboo tar for adsorption of toluene. J Air Waste Manage 63: 977–983. doi: 10.1080/10962247.2013.804011
[44]	Zhang C, Song W, Sun G, et al. (2014) Synthesis, characterization, and evaluation of activated carbon spheres for removal of dibenzothiophene from model diesel fuel. Ind Eng Chem Res 53: 4271–4276. doi: 10.1021/ie403773f
[45]	Zhang C, Song W, Zhang X, et al. (2018) Synthesis, characterization and evaluation of resin-based carbon spheres modified by oxygen functional groups for gaseous elemental mercury capture. J Mater Sci 53: 9429–9448. doi: 10.1007/s10853-018-2231-6
[46]	Zhang C, Song W, Zhang X, et al. (2018) Synthesis and evaluation of activated carbon spheres with copper modification for gaseous elemental mercury removal. J Porous Mat 2018: 1–11.
[47]	Mestre AS, Tyszko E, Andrade MA, et al. (2015) Sustainable activated carbons prepared from a sucrose-derived hydrochar: Remarkable adsorbents for pharmaceutical compounds. RSC Adv 5: 19696–19707. doi: 10.1039/C4RA14495C
[48]	Romero-Anaya AJ, Lillo-Ródenas MA, Linares-Solano A (2014) Activation of a spherical carbon for toluene adsorption at low concentration. Carbon 77: 616–626. doi: 10.1016/j.carbon.2014.05.066
[49]	Liu J, Sun N, Sun C, et al. (2015) Spherical potassium intercalated activated carbon beads for pulverised fuel CO₂ post-combustion capture. Carbon 94: 243–255. doi: 10.1016/j.carbon.2015.06.036
[50]	Wang Q, Liang X, Qiao W, et al. (2009) Preparation of polystyrene-based activated carbon spheres with high surface area and their adsorption to dibenzothiophene. Fuel Process Technol 90: 381–387. doi: 10.1016/j.fuproc.2008.10.008
[51]	Wang Q, Liang X, Zhang R, et al. (2009) Preparation of polystyrene-based activated carbon spheres and their adsorption of dibenzothiophene. New Carbon Mater 24: 55–60. doi: 10.1016/S1872-5805(08)60036-0
[52]	Yang JB, Ling LC, Liu L, et al. (2002) Preparation and properties of phenolic resin-based activated carbon spheres with controlled pore size distribution. Carbon 40: 911–916. doi: 10.1016/S0008-6223(01)00222-6
[53]	Menya E, Olupot PW, Storz H, et al. (2018) Production and performance of activated carbon from rice husks for removal of natural organic matter from water: A review. Chem Eng Res Des 129: 271–296. doi: 10.1016/j.cherd.2017.11.008
[54]	Shi Y, Zhang X, Liu G (2015) Activated carbons derived from hydrothermally carbonized sucrose: Remarkable adsorbents for adsorptive desulfurization. ACS Sustain Chem Eng 3: 2237–2246. doi: 10.1021/acssuschemeng.5b00670
[55]	Zhang C, Lin S, Peng J, et al. (2017) Preparation of highly porous carbon through activation of NH₄Cl induced hydrothermal microsphere derivation of glucose. RSC Adv 7: 6486–6491. doi: 10.1039/C6RA26141H
[56]	Fan Y, Liu PF, Yang ZJ, et al. (2015) Bi-functional porous carbon spheres derived from pectin as electrode material for supercapacitors and support material for Pt nanowires towards electrocatalytic methanol and ethanol oxidation. Electrochim Acta 163: 140–148. doi: 10.1016/j.electacta.2015.02.157
[57]	Chowdhury ZZ, Hamid SBA, Rahman MM, et al. (2016) Catalytic activation and application of micro-spherical carbon derived from hydrothermal carbonization of lignocellulosic biomass: Statistical analysis using Box-Behnken design. RSC Adv 6: 102680–102694. doi: 10.1039/C5RA26189A
[58]	Yang W, Feng Y, Xiao D, et al. (2015) Fabrication of microporous and mesoporous carbon spheres for high-performance supercapacitor electrode materials. Int J Energ Res 39: 805–811. doi: 10.1002/er.3301
[59]	Wang L, Li Y, Yang K, et al. (2017) Hierarchical porous carbon microspheres derived from biomass-corncob as ultra-high performance supercapacitor electrode. Int J Electrochem Sc 12: 5604–5617
[60]	Yang X, Xia H, Liang Z, et al. (2017) Monodisperse carbon nanospheres with hierarchical porous structure as electrode material for supercapacitor. Nanoscale Res Lett 12: 550. doi: 10.1186/s11671-017-2318-z
[61]	Liu M, Gan L, Xiong W, et al. (2013) Nickel-doped activated mesoporous carbon microspheres with partially graphitic structure for supercapacitors. Energ Fuel 27: 1168–1173. doi: 10.1021/ef302028j
[62]	Lin F, Wang Y, Lin Z (2016) One-pot synthesis of nitrogen-enriched carbon spheres for hexavalent chromium removal from aqueous solution. RSC Adv 6: 33055–33062. doi: 10.1039/C5RA27738H
[63]	Ng SWL, Yilmaz G, Ong WL, et al. (2018) One-step activation towards spontaneous etching of hollow and hierarchical porous carbon nanospheres for enhanced pollutant adsorption and energy storage. Appl Catal B-Environ 220: 533–541. doi: 10.1016/j.apcatb.2017.08.069
[64]	Hao ZQ, Cao JP, Zhao XY, et al. (2018) Preparation of porous carbon spheres from 2-keto-l-gulonic acid mother liquor by oxidation and activation for electric double-layer capacitor application. J Colloid Interf Sci 513: 20–27. doi: 10.1016/j.jcis.2017.11.006
[65]	Ma M, Zhang C, Huang G, et al. (2015) Synthesis and electrochemical performance of polyacrylonitrile carbon nanostructure microspheres for supercapacitor application. J Nanomater 2015: 1–10.
[66]	Chang B, Guan D, Tian Y, et al. (2013) Convenient synthesis of porous carbon nanospheres with tunable pore structure and excellent adsorption capacity. J Hazard Mater 262: 256–264. doi: 10.1016/j.jhazmat.2013.08.054
[67]	Wang Y, Chang B, Guan D, et al. (2015) Mesoporous activated carbon spheres derived from resorcinol-formaldehyde resin with high performance for supercapacitors. J Solid State Electr 19: 1783–1791. doi: 10.1007/s10008-015-2789-8
[68]	Kim C, Kim K, Moon JH (2017) Highly N-doped microporous carbon nanospheres with high energy storage and conversion efficiency. Sci Rep 7: 14400. doi: 10.1038/s41598-017-14686-1
[69]	Sun Y, Zhao J, Wang J, et al. (2017) Sulfur-doped millimeter-sized microporous activated carbon spheres derived from sulfonated poly(styrene-divinylbenzene) for CO₂ capture. J Phys Chem C 121: 10000–10009. doi: 10.1021/acs.jpcc.7b02195
[70]	Sun Y, Li K, Zhao J, et al. (2018) Nitrogen and sulfur co-doped microporous activated carbon macro-spheres for CO₂ capture. J Colloid Interf Sci 526: 174–183. doi: 10.1016/j.jcis.2018.04.101
[71]	Thommes M, Kaneko K, Neimark AV, et al. (2015) Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl Chem 87: 1051–1069.
[72]	Oh WC, Kim JG, Kim H, et al. (2009) Preparation of spherical activated carbon and their physicochemical properties. J Korean Ceram Soc 46: 568–573. doi: 10.4191/KCERS.2009.46.6.568
[73]	Dixit S, Shrivastava R, Goswami CS, et al. (2013) Effect of activation parameters on the surface and mechanical properties of activated carbon spheres. Int J Met Mat Sc Eng 3: 75–84.
[74]	Wu Q, Li W, Liu S (2014) Carboxyl-rich carbon microspheres prepared from pentosan with high adsorption capacity for heavy metal ions. Mater Res Bull 60: 516–523. doi: 10.1016/j.materresbull.2014.09.015
[75]	Zhou J, Wang Y, Wang J, et al. (2016) Effective removal of hexavalent chromium from aqueous solutions by adsorption on mesoporous carbon microspheres. J Colloid Interf Sci 462: 200–207. doi: 10.1016/j.jcis.2015.10.001
[76]	Liu MX, Deng XX, Zhu DZ, et al. (2016) Magnetically separated and N,S co-doped mesoporous carbon microspheres for the removal of mercury ions. Chinese Chem Lett 27: 795–800. doi: 10.1016/j.cclet.2016.01.038
[77]	Song X, Gunawan P, Jiang R, et al. (2011) Surface activated carbon nanospheres for fast adsorption of silver ions from aqueous solutions. J Hazard Mater 194: 162–168. doi: 10.1016/j.jhazmat.2011.07.076
[78]	Pan ZZ, Dong L, Lv W, et al. (2017) A hollow spherical carbon derived from the spray drying of corncob lignin for high-rate-performance supercapacitors. Chem-Asian J 12: 503–506. doi: 10.1002/asia.201601724
[79]	Tang J, Wang J, Shrestha LK, et al. (2017) Activated porous carbon spheres with customized mesopores through assembly of diblock copolymers for electrochemical capacitor. ACS Appl Mater Inter 9: 18986–18993. doi: 10.1021/acsami.7b04967
[80]	Ho HC, Goswami M, Chen J, et al. (2018) Amending the structure of renewable carbon from biorefinery waste-streams for energy storage applications. Sci Rep 8: 8355. doi: 10.1038/s41598-018-25880-0
[81]	Zhou L, Xie G, Chen X (2018) Carbonization-dependent nitrogen-doped hollow porous carbon nanospheres synthesis and electrochemical study for supercapacitors. J Solid State Chem 261: 1–8. doi: 10.1016/j.jssc.2018.02.001
[82]	Ruan CQ, Wang Z, Lindh J, et al. (2018) Carbonized cellulose beads for efficient capacitive energy storage. Cellulose 25: 3545–3556. doi: 10.1007/s10570-018-1811-6
[83]	Chen Z, Ye S, Evans SD, et al. (2018) Confined assembly of hollow carbon spheres in carbonaceous nanotube: A spheres-in-tube carbon nanostructure with hierarchical porosity for high-performance supercapacitor. Small 14: 1704015. doi: 10.1002/smll.201704015
[84]	Sun Z, Shen S, Ma L, et al. (2016) Controlled synthesis of N-doped carbon spheres with different morphologies for supercapacitors. RSC Adv 6: 104642–104647. doi: 10.1039/C6RA22424E
[85]	Liu M, Wang X, Zhu D, et al. (2017) Encapsulation of NiO nanoparticles in mesoporous carbon nanospheres for advanced energy storage. Chem Eng J 308: 240–247. doi: 10.1016/j.cej.2016.09.061
[86]	Chen A, Xia K, Zhang L, et al. (2016) Fabrication of nitrogen-doped hollow mesoporous spherical carbon capsules for supercapacitors. Langmuir 32: 8934–8941. doi: 10.1021/acs.langmuir.6b02250
[87]	Hong YJ, Kang YC (2015) General formation of Tin nanoparticles encapsulated in hollow carbon spheres for enhanced lithium storage capability. Small 11: 2157–2163. doi: 10.1002/smll.201402994
[88]	Mutuma BK, Matsoso B, Ranganathan K, et al. (2016) Generation of open-ended, worm-like and graphene-like structures from layered spherical carbon materials. RSC Adv 6: 20399–20408. doi: 10.1039/C5RA25880D
[89]	Pappas GS, Ferrari S, Huang X, et al. (2016) Heteroatom doped-carbon nanospheres as anodes in lithium ion batteries. Materials 9: 35. doi: 10.3390/ma9010035
[90]	Kim MH, Kim KB, Park SM, et al. (2016) Hierarchically structured activated carbon for ultracapacitors. Sci Rep 6: 21182. doi: 10.1038/srep21182
[91]	Chen XY, Chen C, Zhang ZJ, et al. (2013) Nitrogen-doped porous carbon spheres derived from polyacrylamide. Ind Eng Chem Res 52: 12025–12031. doi: 10.1021/ie4017013
[92]	Chang B, Yang B, Guo Y, et al. (2015) Preparation and enhanced supercapacitance performance of porous carbon spheres with a high degree of graphitization. RSC Adv 5: 2088–2095. doi: 10.1039/C4RA09204J
[93]	Ren W, Zhang Z, Wang Y, et al. (2015) Preparation of porous silicon/carbon microspheres as high performance anode materials for lithium ion batteries. J Mater Chem A 3: 5859–5865. doi: 10.1039/C4TA07093C
[94]	Wang M, Zhang H, Wang Q, et al. (2015) Steam-etched spherical carbon/sulfur composite with high sulfur capacity and long cycle life for Li/S battery application. ACS Appl Mater Inter 7: 3590–3599. doi: 10.1021/am5075562
[95]	Jia Z, Li Z, Li S, et al. (2016) Adsorption performance and mechanism of methylene blue on chemically activated carbon spheres derived from hydrothermally-prepared poly(vinyl alcohol) microspheres. J Mol Liq 220: 56–62. doi: 10.1016/j.molliq.2016.04.063
[96]	Fu J, Chen Z, Wang M, et al. (2015) Adsorption of methylene blue by a high-efficiency adsorbent (polydopamine microspheres): Kinetics, isotherm, thermodynamics and mechanism analysis. Chem Eng J 259: 53–61. doi: 10.1016/j.cej.2014.07.101
[97]	Wei D, Zhang Y, Fu J (2017) Fabrication of carbon nanospheres by the pyrolysis of polyacrylonitrile-poly(methyl methacrylate) core–shell composite nanoparticles. Beilstein J Nanotech 8: 1897–1908. doi: 10.3762/bjnano.8.190
[98]	Zhang W, Zhou Z (2017) Citrus pectin-derived carbon microspheres with superior adsorption ability for methylene blue. Nanomaterials 7: 161. doi: 10.3390/nano7070161
[99]	Bedin KC, Martins AC, Cazetta AL, et al. (2016) KOH-activated carbon prepared from sucrose spherical carbon: Adsorption equilibrium, kinetic and thermodynamic studies for methylene blue removal. Chem Eng J 286: 476–484. doi: 10.1016/j.cej.2015.10.099
[100]	Shao X, Wang W, Xue R, et al. (2004) Adsorption of methane and hydrogen on mesocarbon microbeads by experiment and molecular simulation. J Phys Chem B 108: 2970–2978. doi: 10.1021/jp035715d
[101]	Choma J, Osuchowski Ł, Dziura A, et al. (2015) Benzene and methane adsorption on ultrahigh surface area carbons prepared from sulphonated styrene divinylbenzene resin by KOH Activation. Adsorpt Sci Technol 33: 587–594. doi: 10.1260/0263-6174.33.6-8.587
[102]	Choma J, Osuchowski Ł, Marszewski M, et al. (2014) Highly microporous polymer-based carbons for CO₂ and H₂ adsorption. RSC Adv 4: 14795. doi: 10.1039/c3ra47278g
[103]	Wang ZQ, Sun LX, Xu F, et al. (2016) The synthesis of nitrogen-doped mesoporous carbon spheres for hydrogen storage. Mater Sci Forum 852: 864–869. doi: 10.4028/www.scientific.net/MSF.852.864
[104]	Sun N, Sun C, Liu J, et al. (2015) Surface-modified spherical activated carbon materials for pre-combustion carbon dioxide capture. RSC Adv 5: 33681–33690. doi: 10.1039/C5RA02665B
[105]	Jahandar LM, Atkinson JD, Hashisho Z, et al. (2016) The role of beaded activated carbon's surface oxygen groups on irreversible adsorption of organic vapors. J Hazard Mater 317: 284–294. doi: 10.1016/j.jhazmat.2016.05.087
[106]	Romero-Anaya AJ, Lillo-Ródenas MA, Linares-Solano A (2015) Factors governing the adsorption of ethanol on spherical activated carbons. Carbon 83: 240–249. doi: 10.1016/j.carbon.2014.10.092
[107]	Jahandar LM, Atkinson JD, Hashisho Z, et al. (2016) The role of beaded activated carbon's pore size distribution on heel formation during cyclic adsorption/desorption of organic vapors. J Hazard Mater 315: 42–51. doi: 10.1016/j.jhazmat.2016.04.071
[108]	Qi J, Li J, Li Y, et al. (2017) Synthesis of porous carbon beads with controllable pore structure for volatile organic compounds removal. Chem Eng J 307: 989–998. doi: 10.1016/j.cej.2016.09.022
[109]	Zhang P, Zhu H, Dai S (2015) Porous carbon supports: Recent advances with various morphologies and compositions. ChemCatChem 7: 2788–2805. doi: 10.1002/cctc.201500368
[110]	Munoz M, Kolb V, Lamolda A, et al. (2017) Polymer-based spherical activated carbon as catalytic support for hydrodechlorination reactions. Appl Catal B-Environ 218: 498–505. doi: 10.1016/j.apcatb.2017.07.001
[111]	Hadidi L, Mahmoud AYF, Purkait TK, et al. (2017) Cellulose nanocrystal-derived hollow mesoporous carbon spheres and their application as a metal-free catalyst. Nanotechnology 28: 505606. doi: 10.1088/1361-6528/aa95a2
[112]	Yang S, Zhu Y, Cao C, et al. (2018) Controllable synthesis of multiheteroatoms co-doped hierarchical porous carbon spheres as an ideal catalysis platform. ACS Appl Mater Inter 10: 19664–19672. doi: 10.1021/acsami.8b03283
[113]	Veerakumar P, Muthuselvam P, Pounraj T, et al. (2018) Low-cost palladium decorated on m-aminophenol-formaldehyde-derived porous carbon spheres for the enhanced catalytic reduction of organic dyes. Inorg Chem Front 5: 354–363. doi: 10.1039/C7QI00553A
[114]	Galeano C, Meier JC, Soorholtz M, et al. (2014) Nitrogen-doped hollow carbon spheres as a support for platinum-based electrocatalysts. ACS Catal 4: 3856–3868. doi: 10.1021/cs5003492
[115]	With PC, Wilde N, Modrow A, et al. (2015) Polymer-based spherical activated carbons in combination with TS-1 as efficient epoxidation catalysts. Chem Eng Technol 38: 1671–1676. doi: 10.1002/ceat.201500366
[116]	Wang X, Xin C, Shi C, et al. (2018) Simple preparation of spherical activated carbon with mesoporous structure from phenolic resol and associated catalytic performance in isobutane dehydrogenation. Trans Tianjin Univ 24: 351–360. doi: 10.1007/s12209-018-0144-8
[117]	Zhao Q, Lin Y, Han N, et al. (2017) Mesoporous carbon nanomaterials in drug delivery and biomedical application. Drug Deliv 24: 94–107. doi: 10.1080/10717544.2017.1399300
[118]	Yamamoto O, Sawai J, Sasamoto T (2002) Activated carbon sphere with antibacterial characteristics. Mater Trans 43: 1069–1063. doi: 10.2320/matertrans.43.1069
[119]	Yamaguchi J, Tanaka T, Inagi R (2017) Effect of AST-120 in chronic kidney disease treatment: Still a controversy? Nephron 135: 201–206. doi: 10.1159/000453673
[120]	Schute K, Louven Y, Detoni C, et al. (2016) Selective liquid phase adsorption of biogenic HMF on hydrophobic spherical activated carbons. Chem Ing Tech 88: 355–362. doi: 10.1002/cite.201500133
[121]	Meng Y, Wang S, Li C, et al. (2016) Photothermal combined gene therapy achieved by polyethyleneimine-grafted oxidized mesoporous carbon nanospheres. Biomaterials 100: 134–142. doi: 10.1016/j.biomaterials.2016.05.033
[122]	Wang T, Zhao P, Zhao Q, et al. (2016) The mechanism for increasing the oral bioavailability of poorly water-soluble drugs using uniform mesoporous carbon spheres as a carrier. Drug Deliv 23: 420–428. doi: 10.3109/10717544.2014.916767
[123]	Karkalić R, Maslak V, Nikolić A, et al. (2015) Application of permeable materials for CBRN protective equipment. Zast Mater 56: 239–242.
[124]	Fernández JF, Nierobisch P, Niemeyer B (2014) Performance evaluation of protective clothing against toxic industrial chemicals. Chem Ing Tech 86: 35–40. doi: 10.1002/cite.201300055
[125]	Fichtner S, Hofmann J, Möller A, et al. (2013) Decomposition of 2-chloroethylethylsulfide on copper oxides to detoxify polymer-based spherical activated carbons from chemical warfare agents. J Hazard Mater 262: 789–795. doi: 10.1016/j.jhazmat.2013.09.052
[126]	Tagliavini M, Engel F, Weidler PG, et al. (2017) Adsorption of steroid micropollutants on polymer-based spherical activated carbon (PBSAC). J Hazard Mater 337: 126–137. doi: 10.1016/j.jhazmat.2017.03.036

Reader Comments

Your name:*

Email:*
© 2018 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)